文献综述（或调研报告）：
混凝土模拟液中钼酸盐对钢筋的阻锈能力研究
——文献综述
（12015127 马海峰）
（指导教师：施锦杰）
摘要：钢筋锈蚀是影响钢筋混凝土耐久性的一大问题，每年钢筋生锈问题都会造成严重的经济损失。常用的阻锈方法有混凝土表面防护、电化学防护、钢筋表面涂镀和添加阻锈剂等。而在各种阻锈方法中，添加阻锈剂因其施工简单、成本可控且阻锈效果良好，是一种常用方法。目前使用较多的阻锈剂如亚硝酸盐等，具有毒性，破坏环境，而钼酸盐阻锈剂因其无毒、阻锈效果好，是传统阻锈剂的良好替代品。本文从钢筋锈蚀角度出发，介绍了钼酸盐阻锈剂的使用情况及国内外的研究现状。
关键词：钢筋锈蚀；阻锈剂；钼酸盐；研究现状
Abstract：Corrosion of steel bar is a vital problem to reinforced concretersquo;s durability, and it makes serious economic losses every year. In practice, concrete service protection, electrochemical protection, coating on rebar and corrosion inhibitors are used to delay corrosion. Among various ways about corrosion inhibition, adding corrosion inhibitor is a usual method because of the simple construction, appropriate cost and good effect on corrosion inhibition. But frequently-used inhibitors such as nitrite are toxic and unfriendly to environment while molybdates have a great effect on steel corrosion and no toxicity to environment, which is ideal substitute. This article starts on steel corrosion situation, and will introduce the present application of molybdate inhibitor and the research status at home and aboard.
Keywords: steel bar corrosion; corrosion inhibitor; molybdate; research status
- 总述
钢筋混凝土结构是目前土木工程行业使用最广泛的结构，由于其优异的力学性能和相对低廉的造价成为工程建设的最佳选择。但在钢筋混凝土结构服役使用过程中可能会接触到腐蚀介质而引起钢筋锈蚀，在影响混凝土耐久性的各种因素中，钢筋锈蚀被认为是导致混凝土结构达不到预期寿命提前破坏的首要原因[1][2]。目前有很多延缓钢筋锈蚀的方法，包括提高混凝土密实性、混凝土表面防护、钢筋镀膜或增加涂层、阴极保护、阻锈剂等[2]，其中添加阻锈剂是一种高效且操作简单的方法，是目前研究的一大方向。现在应用广泛的阻锈剂存在成本、毒性等问题，而钼酸盐阻锈剂无毒、环境友好，是阻锈剂的一个良好选择[3]，本文将总结钼酸盐的应用优势及国内外研究现状。
以上是毕业论文文献综述，课题毕业论文、任务书、外文翻译、程序设计、图纸设计等资料可联系客服协助查找。